Abstract:

The development of anti-solvent free, scalable, and printable perovskite film is crucial to realizing the low-cost roll-to-roll development of perovskite solar cells (PSCs). Herein, large-area perovskite film fabrication is explored using a spray-assisted sequential deposition technique. How propylene carbonate (PC) solvent additive affects the transformation of lead halide (PbI₂ ) into perovskite at room temperature is investigated. The result shows that PC-modified perovskite films exhibit a uniform, pinhole-free morphology with oriented grains compared with pristine perovskite films. The PC-modified perovskite film also has a prolonged fluorescence lifetime that indicates lower carrier recombination. The champion PSC devices based on PC-modified perovskite film realize a power conversion efficiency (PCE) of 20.5% and 19.3% at an active area (A) of 0.09 cm² and 1 cm² , respectively. The fabricated PSCs are stable and demonstrate ≥85% PCE retention following 60 days of exposure to ambient conditions. Furthermore, perovskite solar modules (A ≈ 13 cm² ) that yield a PCE of 15.8% are fabricated. These results are among the best reported for the state-of-art spray-coated PSCs. Spray deposition coupled with a PC additive is highly promising for economical and high-output preparation of PSCs.

Abstract:

An open-cage bis[60]fulleroid (OC) was applied as electron transport material (ETM) in tin (Sn) halide perovskite solar cells (PSCs). Due to the reduced offset between the energy levels of Sn-based...

Abstract:

Perovskite solar cells (PSCs) comprise a solid perovskite absorber sandwiched between several layers of different charge-selective materials, ensuring unidirectional current flow and high voltage output of the devices. A ‘buffer material’ between the electron-selective layer and the metal electrode in p-type/intrinsic/n-type (p-i-n) PSCs (also known as inverted PSCs) enables electrons to flow from the electron-selective layer to the electrode. Furthermore, it acts as a barrier inhibiting the inter-diffusion of harmful species into or degradation products out of the perovskite absorber. Thus far, evaporable organic molecules and atomic-layer-deposited metal oxides have been successful, but each has specific imperfections. Here we report a chemically stable and multifunctional buffer material, ytterbium oxide (YbOx), for p-i-n PSCs by scalable thermal evaporation deposition. We used this YbOx buffer in the p-i-n PSCs with a narrow-bandgap perovskite absorber, yielding a certified power conversion efficiency of more than 25%. We also demonstrate the broad applicability of YbOx in enabling highly efficient PSCs from various types of perovskite absorber layer, delivering state-of-the-art efficiencies of 20.1% for the wide-bandgap perovskite absorber and 22.1% for the mid-bandgap perovskite absorber, respectively. Moreover, when subjected to ISOS-L-3 accelerated ageing, encapsulated devices with YbOx exhibit markedly enhanced device stability.